Nickle Alloy Gasket Rings Monel K500 Valve Covers Static Joints DIN 2.4375
Nickle Alloy Gasket Rings, a gasket is a type of sealing component used to create a barrier between one mating surface and another to prevent the escape or ingress of fluids or gases. To accommodate these flat surfaces, the gasket can be flat or slightly curved. They can also be cut into different shapes to fit precisely between the surfaces they’re meant to seal. They can even be made to fit complex mating surfaces. When compressed, gaskets fill in any irregularities or imperfections on the mating surfaces to create a seal. Gaskets must be able to withstand the pressure differentials that occur across the sealing interface. They should maintain their ability to provide an effective seal even under high-pressure conditions to prevent leaks and ensure system integrity.
Applications Of Gasket Rings:
Gaskets are used across different industries that range from automotive to electronics.
- Engine components
- EV battery packs & compartments
- Power generators
- Electronics
- Telecommunication devices
- Transportation & automotive
- Medical devices
- Food & beverage Industry
- Flange & pipe connections
- Valve covers
- Static joints
Monel K500, is a age-hardenablenickel-copper alloy that combines the corrosion resistanceproperties of Monel 400 with high strength corrosion fatigue and erosion resistance properties. It is precipitation hardenable through theadditions of aluminum and titanium. The chemica composition of It retains the excellent corrosionresistant characteristics of alloy 400.When compared with Monel 400, it has enhanced strength and hardnessafter precipitation hardening. It has approximately three times the yield strength and doublethe tensile strength of alloy 400.It can befurther strengthened oy cold working before the orecipitation hardening. It should be annealed when welded and theweldment then stress relieved before aging.
Applications:
Typical applications for Monel K500 that take advantage ofhigh strength and corrosion resistance are pump shafts,impellers, propeller shafts, valve components for ships andoffshore drilling towers, bolting, oil well drill collars, andinstrumentation components for oil and gas production.ltis particularly well suited for centrifugal pumps in themarine industry because of its high strength and low corrosion rates in high-velocity sea water.
High Performance Alloys stocks Alloy K500 in a range otcold drawn, annealed and aged, and hot finished andaged. Material can be supplied in random lengths, cut to order or machined to your specifications. Machining includes drilling, turning, tapping, threading, CNC shapes,flanges, and more. Pump shafts, impellers, propeller shafts. Pumps and valves used in the manufacture of perchlorethylene,chlorinated plastics. Valve components for ships and offshore drilling towers. Instrumentation components for oil and gas production. Oil well drill collars. Particularly well suited for centrifugal pumps.Equipment for processes utilising halide or acid catalysts.
Machining:
Nickel based alloys can be difficult tomachinine.However, it should be emphasized that thesealloys can be machined using conventional productionmethods at satisfactory rates. These alloys harden rapidlygenerate high heat during cutting, weld to the cuttingtool surface and offer high resistance to metal removabecause of their high shear strengths. The following arekey points which should be considered during machining operations: capacity/tools/positive cut/lubrication.
Chemical Composition:
| Element | Ni | Cu | C | Mn | Fe | S | Si | Al | Ti |
| Minimum(%) | 63 | 27 | - | - | - | - | - | 2.3 | 0.35 |
| Max(%) | - | 33 | 0.25 | 1.5 | 2.0 | 0.01 | 0.5 | 3.15 | 0.85 |
Magnetic Characteristics of MONEL alloy K-500:
| Condition | Tensile Strength, ksi | Permeabilitya | Curie Temperature, °F for Permeability of |
| 1.01 | 1.02 | 1.05 | 1.1 |
| Annealed, Quenched | 92.5 | 1.0011 | -210 | -210 | - | - |
| Annealed, Age-Hardened | 151.0 | 1.0018 | -153 | -178 | -202 | -210 |
| Cold-Drawn 20% | 137.0 | 1.0011 | -210 | - | - | - |
| Cold-Drawn 20% and AgeHardened | 186.5 | 1.0019 | -130 | -150 | -182 | -210 |
| Cold-Drawn 50% | 151.3 | 1.0010 | -210 | - | - | - |
| Cold-Drawn 50% and AgeHardened | 198.0 | 1.0019 | -130 | -150 | -182 | -210 |
Recommended Tool Types & Machining Conditions:
| Operations | Carbide Tools |
| Roughing, with severeinterruption | Turning or Facing C-2 andC-3 grade: Negative rakesquare insert, 45° SCEA1,1/32 in. nose radius. Tooholder: 5° neg. back rake5° neg. side rake. Speed:30-50 sfm,0.004-0.008 in.feed, 0.150 in depth of cut.Dry2, oil3, or water-base coolant 4. |
| Normal roughing | Turning or Facing C-2 orC-3 grade: Negative ratesquare insert, 45° SCEA,1/32 in nose radius. Tooholder: 5° neg. back rake5° neg. side rake. Speed:90 sfm depending on rigidity of set up, 0.010 infeed, 0.150 in. depth ofcut. Dry, oil, or water-base coolant. |
| Finishing | Turning or Facing C-2 0rC-3 grade: Positive rakesquare insert, if possible45° SCEA, 1/32 in.noseradius. Tool holder: 5° pos.back rake, 5° pos. siderake.Speed: 95-110 sfm0.005-0.007 in. feed,0.040 in. depth of cut. Dryor water-base coolant. |
| Rough Boring | C-2 or C-3 grade: lf inserttype boring bar, use standard positive raketools with largest possibleSCEA and 1/16 in. nose radius. lf brazed tool bargrind 0° back rake, 10° posside rake, 1/32 in. nose radius and largest possible SCEA.Speed: 70 sfm depending on the rigidityof setup, 0.005-0.008 infeed, 1/8 in. depth of cut.Dry, oil or water-base coolant. |
| Finish Boring | C-2 or C-3 grade: Usestandard positive raketools on insert type bars.Grind brazed tools as fofinish turning and facingexcept back rake may bebest at 0°. Speed: 95-110sfm,0.002-0.004 in feed.Water-base coolant. |